ASTM B196(CuBe2) Beryllium Copper Round Rod 20mmx2000mm In AT(TF00) State

Product Normal Description:

Product Name: Beryllium copper round rod

Grade: CuBe2, ASTM B194

Dia.: 20mm

Length: 2000mm

State: AT(TF00)

Product Brand: CUBERYLLIUM®

CUBERYLLIUM®, as a beryllium copper factory, offers the unparalleled precision with a fast and cost-effective method for supply high quality beryllium copper. While equipped with the advanced equipments, our factrory provides other beryllium application services(Beryllium Copper Products And Cnc Machining).

Chemical Composition of ASTM B196(CuBe2) Beryllium Copper Alloy:

Product Grade: CUBERYLLIUM ®-172(UNS. C17200)

Beryllium(Be): 1.80-2.00%

Cobalt(Co) + Nickel(Ni): 0.20% Min

Cobalt(Co) + Nickel(Ni) + Iron(Fe): 0.60% Max

Lead: 0.02% Max

Copper(Cu): Balance

Note: Copper plus additions equal 99.5% Minimum.

The “King” of all high-strength Copper Alloys, C17200 (AMS 4590 / AMS 4530) non-magnetic alloy offers the best of all worlds when it comes to engineering requirements. Strength, conductivity, ductility, corrosion resistance, machineability, and form-ability—all rival most any other alloy, Copper or otherwise.

Typical Physical Properties of ASTM B196(CuBe2) Beryllium Copper Alloy:

Mechanical and Electrical Properties of ASTM B196(CuBe2) Beryllium Copper Round Rod:

The most important Technology of CUBERYLLIUM ®

A: Heat treatment

Heat treatment is the most important process for this alloy system. While all copper alloys are hardenable by cold working, beryllium copper is unique in being hardenable by a simple low temperature thermal treatment. It involves two basic steps. The first is called solution annealing and the second, precipitation or age hardening.

B: Solution Annealing

For the typical alloy CuBe1.9 (1.8- 2%) the alloy is heated between 720°C and 860°C. At this point the contained beryllium is essentially “dissolved” in the copper matrix (alpha phase). By rapidly quenching to room temperature this solid solution structure is retained. The material at this stage is very soft and ductile and can be readily cold worked by drawing, forming rolling, or cold heading. The solution annealing operation is part of the process at the mill and is not typically used by the customer. Temperature, time at temperature, quench rate, grain size, and hardness are all very critical parameters and are tightly controlled by ohmalloy.

C: Age Hardening

Age hardening significantly enhances the material’s strength. This reaction is generally carried out at temperatures between 260°C and 540°C depending on alloy and desired characteristics. This cycle causes the dissolved beryllium to precipitate as a beryllium rich (gamma) phase in the matrix and at the grain boundaries. It is the formation of this precipitate which causes the large increase in material strength. The level of mechanical properties attained is determined by the temperature and time at temperature. It should be recognized that beryllium copper has no room temperature aging characteristics.

Product Photos:

Applications of ASTM B196(CuBe2) Beryllium Copper Alloy:

CUBERYLLIUM ®-172 is usually used for electrical industry, fasteners and industrial.

Electrical Industry: electrical switch and relay blades(switch parts, relay parts), clips, fuse clips, connectors, spring connectors, navigational indstruments, contact bridges, belleville washers;

Fasteners: washers, lock washers, fasteners, retaining rings, roll pins, screws, bolts;

Industrial: pump parts, springs, electrochemical, spline shafts, non sparking safety tools, flexible metal hose, housings for indtruments, bearings, bushings, valve seats, valve stems, disphragms, springs, welding equipment, rolling mill parts, valves, bourdon tubes, wear plates on heavy equipment, bellows.