CW102C Free Machining Copper Beryllium Round Bar As Per EN 12164 For Switch Parts

Product Description:

Name: Free machining copper beryllium round bar

Grade: CW102C

Size: according customers' requirement

End Product Form: Rods/ Bars

Standard: ASTM B196, QQ-C-530

State of product: A(TB00),H(TD04),AT(TF00),HT(TH04)

Processing: Seamless / Welding

Feature: With high strength and high conductivity

Package: Pack in coil+waterproofing winding film+Drier+Wooden Case

• General Characteristics

• C17300 Combines superior machinability with the good fabrication characteristics of C17200. This alloy is manufactured to provide a combination of high strength and hardness properties coupled with superior thermal properties. This range of properties makes C17300 the premier material for copper alloy molds and a wide range of other applications from oil and gas to aerospace.

• Typical Chemical Composition:

Note: Copper plus additions equal 99.5% minimum.

Typical Physical Properties of CW102C Free Machining Copper Beryllium Alloys:

Density: 8.36g/cm3

Density before age hardening: 8.25g/cm3

Melting Range: 870~980℃

Elastic Modulus((kg/mm2 (103)): 13.4

Thermal Expansion Coefficient(20 °C to 200 °C m/m/°C): 17 x 10 -6

Thermal Conductivity(cal/(cm-s-°C)): 0.25

Mechanical and Electrical Properties of CW102C Free Machining Copper Beryllium Round Bar:

Product Photo:

CW102C Free Machining Copper Beryllium Alloys International Specification:

Rods/Bars/Tubes: ASTM B196, QQ-C-530

Wires: ASTM B197, QQ-C-530

European Standards: CuBe2Pb, Alloy M25, UNS.C17300, DIN.2.1248, CW102C to EN

Note:

ASTM: American Society for Testing and Materials

SAE: Society of Automotive Engineers

AMS: Aerospace Materials Specification(Published by SEA)

RWMA: Resistance Welder Manufacturers' Association

Note: Unless otherwise specified, material will be produced by ASTM.

Key Technology of Beryllium Copper(Heat treatment)

Age Hardening

Age hardening significantly enhances the material’s strength. This reaction is generally carried out at temperatures between 260°C and 540°C depending on alloy and desired characteristics. This cycle causes the dissolved beryllium to precipitate as a beryllium rich (gamma) phase in the matrix and at the grain boundaries. It is the formation of this precipitate which causes the large increase in material strength. The level of mechanical properties attained is determined by the temperature and time at temperature. It should be recognized that beryllium copper has no room temperature aging characteristics.

FAQ:

Q1:What’s the advantages the Beryllium Copper of CUBERYLLIUM®?

A1: 1: The Biggest Coil weight could be reach 1200kg/Coil.

2:We are the only one who melting by Vacuum semi-Continuous Furnace.

3:Surface further polishing for top clients.

Q2: How about your payment terms?
A2: Generally, 30% as deposit by T/T, then 70% should be paid before the delivery.

Q3: Why you melting by Vacuum semi-Continuous Furnace?
A3:Could be get the Cast ingot without gas,smaller segregation, Grain Refinement

Q4: What's the payment terms?
A4: We accept T/T, L/C, Paypal etc. It can be negotiated when the amount is different.