⇔ High tensile energy absorption
⇔ Excellent runnability when working on the machine
⇔ Strong strength
⇔ A smooth paper surface and uniform paper formation achieve a high-quality print result
⇔ Virgin wood pulp raw material
⇔ High tear resistance Strong Load-bearing capacity
70gsm 75gsm Semi Extensible Kraft Paper | |||||||||
Properties | Unit | Test Method | Typical Values | ||||||
Basis Weight | g/㎡ | ISO536 | 50 | 60 | 70 | 80 | 90 | 100 | |
Tensile Strength | kN/m | ISO 1924-3 | MD | 4.0 | 4.8 | 5.6 | 6.4 | 7.2 | 8 |
CD | 2.9 | 3.48 | 4.06 | 4.64 | 5.22 | 5.8 | |||
Tensile Index | Nm/g | ISO 1924-3 | MD | 80 | 80 | 80 | 80 | 80 | 80 |
CD | 58 | 58 | 58 | 58 | 58 | 58 | |||
Stretch at break | % | ISO 1924-3 | MD | 5.8 | 5.8 | 5.8 | 5.8 | 5.8 | 5.8 |
CD | 7.4 | 7.4 | 7.4 | 7.4 | 7.4 | 7.4 | |||
Tensile Energy Absorption(TEA) | J/㎡ | ISO 1924-3 | MD | 140 | 170 | 200 | 230 | 260 | 290 |
CD | 170 | 170 | 200 | 230 | 260 | 290 | |||
TEA Index | J/g | ISO 1924-3 | MD | 2.9 | 2.9 | 2.9 | 2.9 | 2.9 | 2.9 |
CD | 2.9 | 2.9 | 2.9 | 2.9 | 2.9 | 2.9 | |||
Tear Index | mN.㎡/g | ISO1974 | MD | 10.5 | 10.5 | 10.5 | 10.5 | 10.5 | 10.5 |
CD | 11.5 | 11.5 | 11.5 | 11.5 | 12 | 12 | |||
Air Resistance | s | ISO 5636-5 | 15 | 15 | 15 | 15 | 15 | 15 | |
Cobb-60" | g/㎡ | ISO535 | 32 | 32 | 32 | 32 | 32 | 32 | |
The table above shows typical values for certain basis weights. | |||||||||
Validity:25.12.2013-31.12.2014 | Test conditions:ISO 554-1976(23 ± 1℃/50 ± 2%) | ||||||||
MD=Machine Direction CD=Cross Direction |