Isostatic Pressing Alumina Custom Ceramic Arc Splitter Shell For Contactor

Specifications

Brand Name :

Antaeus

Model Number :

AD-C023

Certification :

Place of Origin :

Hunan,China

MOQ :

Negotiation

Price :

Negotiation

Payment Terms :

T/T or Negotiation

Supply Ability :

Full Supply

Delivery Time :

15-45 days

Packaging Details :

Inner vacuum packaging, outside carton.

Product Name :

Customized Ceramic Component/ 99 Alumina Ceramic Parts / Structural Machining Ceramic Parts/

Heat Expansion Rate (10-6K-1): :

Tensile :

30 Kpsi - 32 Kpsi

Flexural :

55 Kpsi - 60 Kpsi

Compressive :

300 Kpsi - 330 Kpsi

Density :

6.0g/cm3 And 3.9g/cm3

Fine-machining :

CNC

Forming Process :

Isostatic Pressing

C.O.T.E :

75 In / In°C (x10^7) - 78 In / In°C (x10^7)

Working Temperature :

1500 °C - 1750 °C

Dielectric Constant :

9.5 - 9.8

Volume Resistivity :

>10^14 Ohm-cm

Dielectric Strength :

16 KV/mm - 20 KV/mm

Description

Hot Press Molding Alumina Custom Ceramic Arc Splitter Shell for Contactor

1. Description:

Ceramic is an inorganic non - metallic material which is formed in a firing cycle at high temperature. They are composed of two or more metals. Therefore, the structure of ceramics are more complex than other metals. Ceramics which we used in ancient time was known as traditional ceramic that includes pottery, clay products, (tiles, bricks) cement and silicate glasses. Ceramics that we use nowadays are called advanced ceramics, Technical or Engineering ceramics and Fine ceramics.

2. Feature Advantages:

1) High hardness

2) High elastic modulus

3) Low ductility

4) High dimensional stability

5) Good wear resistance

6) High resistance to corrosion and chemical attack

3. Material Features / Properties:

Composite	(wt %)	99%	99.5%	99.8%
Color		White or Ivory	White or Ivory	White or Ivory
Density	g/cm 3	3.82	3.9	3.92
Hardness	HRA	83	85	85
Flexural Strength	Mpa (psi*10 3 )	375	386	381

4. Technical Parameters:

Technical Parameters of Ceramics
Items	Test Conditions	Unit or Symbol	99% AL2O3	95% AL2O3	90% AL2O3	Zirconia	Steatite	Silicon Carbide
Volume Density	--	g/cm3	≥3.70	≥3.62	≥3.40	≥5.90	≥2.60	≥3.08
Tightness	--	Pa·m³/s	≤1.0×10-11	≤1.0×10-11	≤1.0×10-11	-	-	-
Liquid Permeability	--	--	Pass	Pass	Pass		Pass	-
Flexural Strength	-	MPa	≥300	≥280	≥230	≥1100	≥120	≥400
Elastic Modulus	-	GPa	-	≥280	≥250	≥220	-	400
Poisson Ratio	-	-	-	0.20～0.25	0.20～0.25	-	-	-
Thermal Shock Resistance	800℃( Room Temperature) Cycle: 10 times		Pass	Pass	Pass	-	-	-
Coefficient of Linear Expansion	20℃～100℃	×10-6 K-1	-	-	-		≤8	-
	20℃～500℃	×10-6 K-1	6.5～7.5	6.5～7.5	6.5～7.5	6.5～11.2	-	-
	20℃～800℃	×10-6 K-1	6.5～8.0	6.5～8.0	6.3～7.3		-	4
	20℃～1200℃	×10-6 K-1	-	7.0～8.5	-	-	-	-
Coefficient of Thermal Conductivity	20℃	W/(m·k)	-	-	-	-	-	90～110
Coefficient of Thermal Conductivity	1000℃	W/(m·k)	-	-	-	-	-	90～110
Dielectric Constant	1MHz 20℃	-	9.0～10.5	9.0～10	9.0～10	-	≤7.5	-
	1MHz 50℃	-	-	9.0～10	-	-	-	-
	10GHz 20℃	-	9.0～10.5	9.0～10	9.0～10	-	-	-
Volume Resistivity	100℃	Ω·cm	≥1.0×1013	≥1.0×1013	≥1.0×1013	-	≥1.0×1012	-
	300℃		≥1.0×1013	≥1.0×1010	≥1.0×1013	-	-	-
	500℃		≥1.0×109	≥1.0×108	--	-	-	-
Disruptive Strength	D.C	kV/mm	≥17	≥15	≥15	-	≥20	-
Chemical Durability	1:9HCl	mg/c㎡	≤0.7	≤7.0	-	-	-	-
Chemical Durability	10%NaOH	mg/c㎡	≤0.1	≤0.2	-	--	-	-
Grain Size	-	μm	-	3~12	-	-	-	-

5. Process Flows:

Formulating --- Granulating --- Forming --- Sintering --- Grinding --- Printing --- Nickel Plating --- Assembing --- Brazing --- Inspecting --- Packing