Machining Alumina Advanced Engineering Ceramics Parts High Stiffness ISO14001

Specifications

Brand Name :

Antaeus

Model Number :

AD-E012

Certification :

Place of Origin :

Hunan,China

MOQ :

Negotiation

Price :

Negotiation

Payment Terms :

T/T or Negotiation

Supply Ability :

Full Supply

Delivery Time :

15-45 days

Packaging Details :

Inner vacuum packaging, outside carton.

Product Name :

Advanced Engineering Ceramics / Special Technical Ceramic Parts

AL2O3 Content :

90% - 99%

Tensile :

30 Kpsi - 32 Kpsi

Flexural :

55 Kpsi - 60 Kpsi

Compressive :

300 Kpsi - 330 Kpsi

Density :

3.7 g/cc - 3.92 g/cc

Hardness :

13.8 HV, Gpa - 18 HV, Gpa

Thermal Conductivity :

25 W/(m K) - 32 W/(m K)

C.O.T.E :

75 In / In°C (x10^7) - 78 In / In°C (x10^7)

Working Temperature :

1500 °C - 1750 °C

Dielectric Constant :

9.5 - 9.8

Volume Resistivity :

>10^14 Ohm-cm

Dielectric Strength :

16 KV/mm - 20 KV/mm

Description

Alumina Advanced Engineering Ceramics / Special Technical Ceramic Parts

1. Description:

Alumina advanced engineering ceramics / special technical ceramic parts widely apply for many different fields.Titanium Silicon Carbide has the high stiffness and high temperature properties expected of ceramics, but also the good thermal and electrical conductivity of metals. The layers that form in this ternary also somewhat inhibit crack propagation – meaning while this material does still experience brittle failure, it is significantly tougher than would be expected from a ceramic.The superconductors we mentioned earlier also have complex crystal structures where a variety of different bond types are present and these are carefully tuned to create electrons which can move through channels in the crystal unimpeded.

Feature Advantages:

1) High hardness and high density

2) Low thermal conductivity

3) Chemical inertness

4) Good wear resistance

5) High Fracture toughness

6) Good insulation performance

7) High temperature resistance

8) A variety of specifications is available

9) Satisfy various technical requests

10) Lower medium spoilage

11) Stiffness texture

12) Chemical inertness

13) Good wear resistance

14) High Fracture toughness

15) Good insulation performance

3. Material Features / Properties:

Composite	(wt %)	99%	99.5%	99.8%
Color		White or Ivory	White or Ivory	White or Ivory
Density	g/cm 3	3.82	3.9	3.92
Hardness	HRA	83	85	85
Flexural Strength	Mpa (psi*10 3 )	375	386	381

4. Technical Parameters:

Technical Parameters of Ceramics
Items	Test Conditions	Unit or Symbol	99% AL2O3	95% AL2O3	90% AL2O3	Zirconia	Steatite	Silicon Carbide
Volume Density	--	g/cm3	≥3.70	≥3.62	≥3.40	≥5.90	≥2.60	≥3.08
Tightness	--	Pa·m³/s	≤1.0×10-11	≤1.0×10-11	≤1.0×10-11	-	-	-
Liquid Permeability	--	--	Pass	Pass	Pass		Pass	-
Flexural Strength	-	MPa	≥300	≥280	≥230	≥1100	≥120	≥400
Elastic Modulus	-	GPa	-	≥280	≥250	≥220	-	400
Poisson Ratio	-	-	-	0.20～0.25	0.20～0.25	-	-	-
Thermal Shock Resistance	800℃( Room Temperature) Cycle: 10 times		Pass	Pass	Pass	-	-	-
Coefficient of Linear Expansion	20℃～100℃	×10-6 K-1	-	-	-		≤8	-
	20℃～500℃	×10-6 K-1	6.5～7.5	6.5～7.5	6.5～7.5	6.5～11.2	-	-
	20℃～800℃	×10-6 K-1	6.5～8.0	6.5～8.0	6.3～7.3		-	4
	20℃～1200℃	×10-6 K-1	-	7.0～8.5	-	-	-	-
Coefficient of Thermal Conductivity	20℃	W/(m·k)	-	-	-	-	-	90～110
Coefficient of Thermal Conductivity	1000℃	W/(m·k)	-	-	-	-	-	90～110
Dielectric Constant	1MHz 20℃	-	9.0～10.5	9.0～10	9.0～10	-	≤7.5	-
	1MHz 50℃	-	-	9.0～10	-	-	-	-
	10GHz 20℃	-	9.0～10.5	9.0～10	9.0～10	-	-	-
Volume Resistivity	100℃	Ω·cm	≥1.0×1013	≥1.0×1013	≥1.0×1013	-	≥1.0×1012	-
	300℃		≥1.0×1013	≥1.0×1010	≥1.0×1013	-	-	-
	500℃		≥1.0×109	≥1.0×108	--	-	-	-
Disruptive Strength	D.C	kV/mm	≥17	≥15	≥15	-	≥20	-
Chemical Durability	1:9HCl	mg/c㎡	≤0.7	≤7.0	-	-	-	-
Chemical Durability	10%NaOH	mg/c㎡	≤0.1	≤0.2	-	--	-	-
Grain Size	-	μm	-	3~12	-	-	-	-

5. Process Flows:

Formulating --- Granulating --- Forming --- Sintering --- Grinding --- Printing --- Nickel Plating --- Assembing --- Brazing --- Inspecting --- Packing