Chemical ingredients :

Al2O3

Max. Use Temp. :

1650℃

Bulk Density :

3.6g/cm3-3.9g/cm3

Water absorption :

ROHS Hardness :

≥85

Flexural strength :

358(52) - 550 Mpa(psix10^3)

Compressive Strength :

2068(300) - 2600(377) Mpa(psix10^3)

Coefficient of thermal expansion :

7.6 - 8.2 / 1X10^-6/℃

Coefficient of thermal conductivity :

16-30.4 / W/m.K

Thermal Shock Resistance :

250℃

Dielectricity constant :

9-9.7 / 1MHz.25℃

Dielectric strength :

8.3(210) - 8.7(220) / ac-kV/mm(ac V/mil)

Volume Resistivity :

>10^13 ohm-cm

Description

EV Alumina Ceramic Relay Housing / High Voltage DC Ceramic Contactor

1. Description:

High-performance components advanced ceramics are meeting the needs for higher-performance critical components in a wide
variety of applications. Through a detailed understanding of the ceramic-metal bonding techniques, such as the metallization process, designers and manufacturers are better able to devise these key components. A thin layer of metal deposited on a ceramic part enables brazing to a metal part that has a different coefficient of thermal expansion.

2. Feature Advantages:

1) High compressive strength.

2) Good advanced ceramic materials

3) Chemical inertness

4) Good wear resistance

5) High Fracture toughness

6) Good insulation performance

3. Material Features / Properties:

Composite	(wt %)	99%	99.5%	99.8%
Color		White or Ivory	White or Ivory	White or Ivory
Density	g/cm 3	3.82	3.9	3.92
Hardness	HRA	83	85	85
Flexural Strength	Mpa (psi*10 3 )	375	386	381

4. Technical Parameters:

Technical Parameters of Ceramics
Items	Test Conditions	Unit or Symbol	99% AL2O3	95% AL2O3	90% AL2O3	Zirconia	Steatite	Silicon Carbide
Volume Density	--	g/cm3	≥3.70	≥3.62	≥3.40	≥5.90	≥2.60	≥3.08
Tightness	--	Pa·m³/s	≤1.0×10-11	≤1.0×10-11	≤1.0×10-11	-	-	-
Liquid Permeability	--	--	Pass	Pass	Pass		Pass	-
Flexural Strength	-	MPa	≥300	≥280	≥230	≥1100	≥120	≥400
Elastic Modulus	-	GPa	-	≥280	≥250	≥220	-	400
Poisson Ratio	-	-	-	0.20～0.25	0.20～0.25	-	-	-
Thermal Shock Resistance	800℃( Room Temperature) Cycle: 10 times		Pass	Pass	Pass	-	-	-
Coefficient of Linear Expansion	20℃～100℃	×10-6 K-1	-	-	-		≤8	-
	20℃～500℃	×10-6 K-1	6.5～7.5	6.5～7.5	6.5～7.5	6.5～11.2	-	-
	20℃～800℃	×10-6 K-1	6.5～8.0	6.5～8.0	6.3～7.3		-	4
	20℃～1200℃	×10-6 K-1	-	7.0～8.5	-	-	-	-
Coefficient of Thermal Conductivity	20℃	W/(m·k)	-	-	-	-	-	90～110
Coefficient of Thermal Conductivity	1000℃	W/(m·k)	-	-	-	-	-	90～110
Dielectric Constant	1MHz 20℃	-	9.0～10.5	9.0～10	9.0～10	-	≤7.5	-
	1MHz 50℃	-	-	9.0～10	-	-	-	-
	10GHz 20℃	-	9.0～10.5	9.0～10	9.0～10	-	-	-
Volume Resistivity	100℃	Ω·cm	≥1.0×1013	≥1.0×1013	≥1.0×1013	-	≥1.0×1012	-
	300℃		≥1.0×1013	≥1.0×1010	≥1.0×1013	-	-	-
	500℃		≥1.0×109	≥1.0×108	--	-	-	-
Disruptive Strength	D.C	kV/mm	≥17	≥15	≥15	-	≥20	-
Chemical Durability	1:9HCl	mg/c㎡	≤0.7	≤7.0	-	-	-	-
Chemical Durability	10%NaOH	mg/c㎡	≤0.1	≤0.2	-	--	-	-
Grain Size	-	μm	-	3~12	-	-	-	-

5. Process Flows:

Formulating --- Granulating --- Forming --- Sintering --- Grinding --- Inspecting --- Packing