MachineU > China Products > Chemicals > Inorganic Chemicals > Non-Metallic Products > Ceramics

Specifications

Brand Name :

Antaeus

Model Number :

AD-B030

Certification :

Place of Origin :

Hunan,China

MOQ :

Negotiation

Price :

Negotiation

Payment Terms :

T/T or Negotiation

Supply Ability :

Full Supply

Delivery Time :

15-45 days

Packaging Details :

Inner vacuum packaging, outside carton.

Product Name :

Metallized Alumina Ceramic Rings / Ceramic Insulators for Battery

Material :

Alumina (Aluminum Oxide, Al2O3)

Insulation Resistance :

1000M Ω（1000VDC)

High Light :

Alumina Ceramic Rings / Metallized Ceramic Insulators / Electrical Ceramic Components

Thermal Shock Resistance room temperature to 850C :

will not burst or leak after five operations

Max. Use Temp. :

1650℃

ROHS Hardness :

≥89

Flexural strength :

550 Mpa(psix10^3)

Compressive Strength :

2600(377) Mpa(psix10^3)

Coefficient of thermal expansion :

8.2 X10^-6/℃

Coefficient of thermal conductivity :

17-30.4 W/m.K

Description

Alumina Seal Ceramic Rings / Industry Insulation Rings

1. Description:

The hardness of high-temperature structural ceramics is much higher than that of metals, and the wear resistance at high temperatures is better than that of metals, and especially better than cemented carbide. Metal and ceramic pair sliding. Under lubricated conditions, not only the wear of ceramics is extremely small, but the wear of metal is also smaller than when metals are paired. Most of the parts of the valve mechanism slide at high speed under high load and insufficient lubrication conditions. It is very suitable for ceramic manufacturing to reduce wear. The main disadvantage of ceramic parts in terms of performance is that they are prone to internal cracks during manufacturing. The internal cracks may propagate under stress and cause brittle failure of parts. In addition, temperature sudden changes caused by changes in engine operating conditions, surface damage caused by wear and foreign objects, etc., may affect the reliability and service life of the parts. By applying ceramic coating, the temperature in the combustion chamber of the engine can be improved, and the working efficiency of the engine can be improved.

2. Feature Advantages:

1) Refractory, High Temperature Resistance, Maximum Used Temperature: 1800 ºC (3272ºF)
2) Hardness Strength, Wear Resistance Up To Mohz 9.0 ; HRA 80-90
3) High Voltage, Good Insulation Performance ,Electrical Resistivity Up To 10∧14 Ohm.Cm
4) High Polished Surface Up To Rz0.8(Ra0.1)
5) Superior Mechanical Strength, MAX 10 MPa.m1/2 Fracture toughness
6) Pressure Resistance, Max 2300MPa compressive strength
7) Anti-High Corrosion Resistance, Such As Acid Alkali Resistance
8) Long Service Life

3. Material Features / Properties:

Composite	(wt %)	99%	99.5%	99.8%
Color		White or Ivory	White or Ivory	White or Ivory
Density	g/cm 3	3.82	3.9	3.92
Hardness	HRA	83	85	85
Flexural Strength	Mpa (psi*10 3 )	375	386	381

4. Technical Parameters:

Technical Parameters of Ceramics
Items	Test Conditions	Unit or Symbol	99% AL2O3	95% AL2O3	90% AL2O3	Zirconia	Steatite	Silicon Carbide
Volume Density	--	g/cm3	≥3.70	≥3.62	≥3.40	≥5.90	≥2.60	≥3.08
Tightness	--	Pa·m³/s	≤1.0×10-11	≤1.0×10-11	≤1.0×10-11	-	-	-
Liquid Permeability	--	--	Pass	Pass	Pass		Pass	-
Flexural Strength	-	MPa	≥300	≥280	≥230	≥1100	≥120	≥400
Elastic Modulus	-	GPa	-	≥280	≥250	≥220	-	400
Poisson Ratio	-	-	-	0.20～0.25	0.20～0.25	-	-	-
Thermal Shock Resistance	800℃( Room Temperature) Cycle: 10 times		Pass	Pass	Pass	-	-	-
Coefficient of Linear Expansion	20℃～100℃	×10-6 K-1	-	-	-		≤8	-
	20℃～500℃	×10-6 K-1	6.5～7.5	6.5～7.5	6.5～7.5	6.5～11.2	-	-
	20℃～800℃	×10-6 K-1	6.5～8.0	6.5～8.0	6.3～7.3		-	4
	20℃～1200℃	×10-6 K-1	-	7.0～8.5	-	-	-	-
Coefficient of Thermal Conductivity	20℃	W/(m·k)	-	-	-	-	-	90～110
Coefficient of Thermal Conductivity	1000℃	W/(m·k)	-	-	-	-	-	90～110
Dielectric Constant	1MHz 20℃	-	9.0～10.5	9.0～10	9.0～10	-	≤7.5	-
	1MHz 50℃	-	-	9.0～10	-	-	-	-
	10GHz 20℃	-	9.0～10.5	9.0～10	9.0～10	-	-	-
Volume Resistivity	100℃	Ω·cm	≥1.0×1013	≥1.0×1013	≥1.0×1013	-	≥1.0×1012	-
	300℃		≥1.0×1013	≥1.0×1010	≥1.0×1013	-	-	-
	500℃		≥1.0×109	≥1.0×108	--	-	-	-
Disruptive Strength	D.C	kV/mm	≥17	≥15	≥15	-	≥20	-
Chemical Durability	1:9HCl	mg/c㎡	≤0.7	≤7.0	-	-	-	-
Chemical Durability	10%NaOH	mg/c㎡	≤0.1	≤0.2	-	--	-	-
Grain Size	-	μm	-	3~12	-	-	-	-

5. Process Flows:

Formulating --- Granulating --- Forming --- Sintering --- Grinding --- Printing --- Nickel Plating --- Assembing --- Brazing --- Inspecting --- Packing