High Purity Zirconia Ceramic Parts 3.9g/cm3 Density Customized

Specifications

Brand Name :

Antaeus

Model Number :

AD-Z042

Certification :

Place of Origin :

Hunan,China

MOQ :

Negotiation

Price :

Negotiation

Payment Terms :

T/T or Negotiation

Supply Ability :

Full Supply

Delivery Time :

15-45 days

Packaging Details :

Inner vacuum packaging, outside carton.

Product Name :

Zirconia Ceramic Parts / Structural Machining Ceramic Parts

Heat Expansion Rate (10-6K-1): :

Tensile :

30 Kpsi - 32 Kpsi

Flexural :

55 Kpsi - 60 Kpsi

Compressive :

300 Kpsi - 330 Kpsi

Density :

6.0g/cm3 And 3.9g/cm3

Fine-machining :

CNC

Forming Process :

Isostatic Pressing

C.O.T.E :

75 In / In°C (x10^7) - 78 In / In°C (x10^7)

Working Temperature :

1500 °C - 1750 °C

Dielectric Constant :

9.5 - 9.8

Volume Resistivity :

>10^14 Ohm-cm

Dielectric Strength :

16 KV/mm - 20 KV/mm

Description

Zirconia Drawing Machine Tower Round , Wire Wheels , Reel.

1. Description:

In the world of technical ceramics, there are two materials that are surpassed only by diamond and cubic boron nitride in terms of hardness – and both are used by Precision Ceramics USA as a base material for a wide range of technical components in an equally wide field of applications.Boron Carbide (B4C) is currently the hardest material produced in tonnage quantities and is the third hardest material known to man after diamond and cubic boron nitride. Not far behind it in the hardness stakes comes silicon carbide (SiC), steeped in history since it was first mass-produced in 1893 and probably the most common of all industrial abrasives.

2. Feature Advantages:

1) High density.

2) High fracture toughness .

3) High hardness High Mechanical Strength.

4) Low thermal conductivity Excellent insulation .

5) Good Wear resistance.

6) Resistant to Corrosion and Chemical Attack.

7) Extreme Temperature Stability.

8) Outstanding Electrical and Electronic Properties.

3. Material Features / Properties:

Composite	(wt %)	99%	99.5%	99.8%
Color		White or Ivory	White or Ivory	White or Ivory
Density	g/cm 3	3.82	3.9	3.92
Hardness	HRA	83	85	85
Flexural Strength	Mpa (psi*10 3 )	375	386	381

4. Technical Parameters:

Technical Parameters of Ceramics
Items	Test Conditions	Unit or Symbol	99% AL2O3	95% AL2O3	90% AL2O3	Zirconia	Steatite	Silicon Carbide
Volume Density	--	g/cm3	≥3.70	≥3.62	≥3.40	≥5.90	≥2.60	≥3.08
Tightness	--	Pa·m³/s	≤1.0×10-11	≤1.0×10-11	≤1.0×10-11	-	-	-
Liquid Permeability	--	--	Pass	Pass	Pass		Pass	-
Flexural Strength	-	MPa	≥300	≥280	≥230	≥1100	≥120	≥400
Elastic Modulus	-	GPa	-	≥280	≥250	≥220	-	400
Poisson Ratio	-	-	-	0.20～0.25	0.20～0.25	-	-	-
Thermal Shock Resistance	800℃( Room Temperature) Cycle: 10 times		Pass	Pass	Pass	-	-	-
Coefficient of Linear Expansion	20℃～100℃	×10-6 K-1	-	-	-		≤8	-
	20℃～500℃	×10-6 K-1	6.5～7.5	6.5～7.5	6.5～7.5	6.5～11.2	-	-
	20℃～800℃	×10-6 K-1	6.5～8.0	6.5～8.0	6.3～7.3		-	4
	20℃～1200℃	×10-6 K-1	-	7.0～8.5	-	-	-	-
Coefficient of Thermal Conductivity	20℃	W/(m·k)	-	-	-	-	-	90～110
Coefficient of Thermal Conductivity	1000℃	W/(m·k)	-	-	-	-	-	90～110
Dielectric Constant	1MHz 20℃	-	9.0～10.5	9.0～10	9.0～10	-	≤7.5	-
	1MHz 50℃	-	-	9.0～10	-	-	-	-
	10GHz 20℃	-	9.0～10.5	9.0～10	9.0～10	-	-	-
Volume Resistivity	100℃	Ω·cm	≥1.0×1013	≥1.0×1013	≥1.0×1013	-	≥1.0×1012	-
	300℃		≥1.0×1013	≥1.0×1010	≥1.0×1013	-	-	-
	500℃		≥1.0×109	≥1.0×108	--	-	-	-
Disruptive Strength	D.C	kV/mm	≥17	≥15	≥15	-	≥20	-
Chemical Durability	1:9HCl	mg/c㎡	≤0.7	≤7.0	-	-	-	-
Chemical Durability	10%NaOH	mg/c㎡	≤0.1	≤0.2	-	--	-	-
Grain Size	-	μm	-	3~12	-	-	-	-

5. Process Flows:

Formulating --- Granulating --- Forming --- Sintering --- Grinding --- Printing --- Nickel Plating --- Assembing --- Brazing --- Inspecting --- Packing