Name :
1530℃ Dental Zirconia Disc
Hardness :
1200HV
Sintering temperature :
1530 ℃
Strength :
1200 MPa
Instrument classification :
Class II
Sample :
offer
Package :
OEM (dental material)
Application :
Dental Areal, Dental lab
Thickness :
10/12/14/16/18/20/22/25mm
Size :
98x10/12/14/16/18/20/22/25
Diameter :
98mm
System :
open/zirkonzahn/Amann/Sirona
Warranty :
5 year
Shape :
Disc
Description

Open system Dental Zirconia HT High Strength Zirocnia Block for Coping

Dental Zirconia Disc

To achieve expected quality, the sintering curves must be followed.

Note: please employ high-temperature furnace specially designed for denture manufacturing. It is good for ceramics sintering to prolong heating up time and cooling time properly.

1. Sintering preparation: Make sure there is enough sintering space to avoid deformation. After dyeing, the restoration must be dried. Do not heat up too quickly for it might result in cracks. Make sure the dust-proof cover is put on the crucible to keep impurity away from restorations
2. After sintering: Following the instruction to lower temperature and take out restorations. Do not reduce furnace temperature too quickly to avoid cracks.

3.The highest temperature: the highest temperature will affect the translucency and dyeing results. Make sure the accurate temperature of every step. Sinter and preserve heat according to the instruction.

High Translucency Dental Zirconia Disc For Anterior Restorarion , Dental Zirconia Blank

YUCERA blanks are made from biocompatible zirconiumdioxyde. The yttrium oxide stabilizing protects the material against cracks and increases the tensile and compressive strength. The special grain size allocation inside the material and the added aluminium oxide also result in extra strength during milling and subsequently in clinical use. The outstanding mechanical characteristics, excellent chemical durability and the unbeaten biocompatibility combined with the translucent color predestine XTCERA as the ideal material provider for dental milling systems.
YUCERA HT translucency, apply to single crown, anterior teeth, inlay/onlay and also veneers.

HT Dental Zirconia Disc

* High translucent

* Brilliant bending strength and economic block

* Suitable for coping and framework

Indications

Coping, Inlay, Onlay, Bridge, Crown

Physical Characteristics

Physical Characteristics

Sintered density 6.07±0.01g/cm³

Bending Strength 1200 MPa

Transmittance 41%

Hardness 1200HV

Sintering temperature 1480~1550℃/recommend 1530℃

Dental Lab 1200 MPa 1200HV 1530℃ Dental Zirconia DiscDental Lab 1200 MPa 1200HV 1530℃ Dental Zirconia Disc

Send your message to this supplier
Send Now

Dental Lab 1200 MPa 1200HV 1530℃ Dental Zirconia Disc

Ask Latest Price
Brand Name :
YUCERA
Model Number :
HT
Certification :
CE/ISO/CFDA
Place of Origin :
CN
MOQ :
Negotiation
Price :
Negotiation
Contact Supplier
Dental Lab 1200 MPa 1200HV 1530℃ Dental Zirconia Disc
Dental Lab 1200 MPa 1200HV 1530℃ Dental Zirconia Disc
Dental Lab 1200 MPa 1200HV 1530℃ Dental Zirconia Disc
Dental Lab 1200 MPa 1200HV 1530℃ Dental Zirconia Disc
Dental Lab 1200 MPa 1200HV 1530℃ Dental Zirconia Disc
Dental Lab 1200 MPa 1200HV 1530℃ Dental Zirconia Disc

Shenzhen Yurucheng Dental Materials Co., Ltd

Verified Supplier
5 Years
guangdong, shenzhen
Since 2017
Business Type :
Manufacturer
Total Annual :
100000000-300000000
Employee Number :
300~500
Certification Level :
Verified Supplier
Contact Supplier
Submit Requirement