Solution for the Motorcycle frame electrophoresis paint

Product Introduction

HL-1607LB/HLS-1701A Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.

It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.

This product features shown below: 

The appearance of the coating is flat, delicate, smooth, uniform high gloss.

Stronganti-corrosionproperties,goodsaltsprayresistanceworkpieceedge.

Excellent leveling coating,good bonding for ceand compatibility with plastic powder

.

The main component Matrix resin:

1,Neutralizing agent: organic acid

2,Solvent: alcohol ether

3,Pigment: carbon black, kaolin, antirust pigment

Product quality data:

Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution

Filling tank proportion and method

⑴ Bath preparation

Ratio:

Resin 800.00-1200.00

Paste 200.00

DI water 2000.00

Total 3400.00

⑵ Ripening conditions

Sample quantity: 3000～3400g
Container: 5L (Diameter 16cm)

Tank temperature:28-30 ℃

Time: 24～48Hr

Mixed conditions: impeller diameter 8cm (speed 200rpm)

(3) Coating conditions

Experimental panel: phosphated cold-rolled steel plate

Tank temperature: 30-35℃

Pole ratio: A/C = 1/2 ~ 1/4

Distance of electrodes: 15cm

ED time: For full immersing 1-3 minutes ( 20 seconds soft start)

Baking conditions:(175-185)℃×(20-30)min (Keeping temperature of parts coated)