Item | Value | ||||||||||||
Thickness,mm | 0.75 | 1.0 | 1.25 | 1.5 | 2.0 | 2.5 | 3.0 | ||||||
Density,g/cm3 | ≥0.94 | ||||||||||||
Tensile yiedl strength,N/mm | ≥11 | ≥15 | ≥18 | ≥22 | ≥29 | ≥37 | ≥44 | ||||||
Tensile breaking strength,N/mm | ≥20 | ≥27 | ≥33 | ≥40 | ≥53 | ≥67 | ≥80 | ||||||
Elongation at yield, % | ≥12 | ||||||||||||
Elongation at break,% | ≥700 | ||||||||||||
Tear Resistance,N | ≥93 | ≥125 | ≥160 | ≥190 | ≥250 | ≥315 | ≥375 | ||||||
Puncture Resistance,N | ≥240 | ≥320 | ≥400 | ≥480 | ≥640 | ≥800 | ≥960 | ||||||
Stress Crack Resistance,h | ≥300 | ||||||||||||
Carbon Black Content, % | 2.0~3.0 | ||||||||||||
Carbon Black Dispersion | 1or 2 | ||||||||||||
Standard OIT,min | ≥100 | ||||||||||||
High Pressure OIT,min | ≥400 |