MachineU > China Products > Chemicals > Inorganic Chemicals > Non-Metallic Products > Refractory
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
Specifications
Place of Origin :
Henan, China
Shape :
Powder
Material :
Diatomite
SiO2 Content (%) :
≤8.0%
Al2O3 Content (%) :
≥50~70
CaO Content (%) :
30% ~ 39%, 30% ~ 39%
Refractoriness (Degree) :
Common (1580°< Refractoriness< 1770°)
Model Number :
A600 A700 A900
Brand Name :
Hongtai
Product name :
High alumina cement A600 A700 A900
Al2O3 Content :
≥50~70
SiO2 Content :
≤8.0%
Fire resistance cement Fe2O3(%) :
<2.5%
Compressive strength MPa :
≥80
Setting time Min :
>30
R2O(Na2O+0.658K2O) :
<0.4
Fire resistance cement Sample :
free
Fire resistance cement OEM :
YES
Price :
$150.00 - $450.00/tons
Description
Product Description

Refractory High alumina cement A600 A700 A900

High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30

High alumina cement, also known as HAC, is a special cement compound that develops strength very quickly. It is produced much in the same way as other forms of cement, but its unique makeup results in characteristics that are unique to HAC. Specifically, high alumina cement is chemical resistant and can withstand frigid temperatures.
High alumina cement are calcined by natural high grade bauxite and limestone as selected raw material. The main phase of this series is CA and CA2 which mainly formed the clinker. After grinded to the best particle size distribution, the cements will meet the demand of the most critical customers.
High alumina cement Properties:
1.High Almina Content
2.High early strength, fast setting and hardening. 24hours strength can reach 70% the ultimate strength.
3.The high heat of hydration, the hydration heat concentration
4.The high heat of hydration with exothermic concentration
5.The frost resistance is good, normal hardening can also in the lower temperature environment
6.Chemical erosion and anti-bio at wide range, especially strong anti sulfate erosion.
7.Ideal for high temperature and thermal shock resistance performance is very admirable , its refractory temperature can reach 1370 ºC. 1500 ºC. can be reached if better refractory aggregate were chosen.
8.Mainly used in formulating monolithic refractory and widely in steel, crude oil, electrical, nonferrous metal, construction and kiln indust
1)Particle size can be customized
2)Chemical and physical index can be customized
3) Testing methods of S, Cl- can be acquired if customer need.

Technical Data

Refractory High alumina cement A600 A700 A900

High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30

tems CA50/A600 CA50/A700 CA50/A900SCA
Al2O3% ≥50.0 ≥50.0 50.0--58.0
CaO% 33.0--35.0 33.0--35.0 33.0--36.0
SiO2% ≤8.0 ≤8.0 5.0--7.5
Fe2O3% ≤2.5 ≤2.5 1.5--2.5
R2O% ≤0.4 ≤0.4 ≤0.4
Setting time(min) Initial set ≥30 ≥30 ≥30
Final set ≤360 ≤360 ≤360
Flexural strength(Mpa) 1 day 6.0 6.5 8.0
3 days 7.0 7.5 9.0
Compressive strength(Mpa) 1 day 45 55 75
3 days 55 65 85
Fineness Residue on Sieve <15 <12 ≤3.0(180mesh)
≤5.0(325mesh)
Specific Area(g/m2) ≥350 ≥350 350-450

High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30

Items CA60 CA70 CA80
Al2O3% 58.0----65.0 ≥68 78--81
CaO% 17.0----25.0 20--25 20--25
SiO2% 5.0----8.0 ≤1.0 ≤2.0
Fe2O3% 1.5----2.5 ≤0.7 ≤0.5
R2O% < 0.4 ≤0.4 ≤0.4
Setting time Initial set ≥ 60min ≥30 ≥30
Final set ≤ 18h ≤360 ≤360
Flexural strength(Mpa) 1 day 2.5 5.0 5.0
3 days 5.0 6.0 6.0
28 days 10.0 - -
Compressive strength(Mpa) 1 day 20 30 45
3 days 45 40 55
28 days 85 - -
Fineness Residue on Sieve ≤ 5.0 ≤3.0(180mesh)
3.0--5.0(325mesh)		 ≤3.0(180mesh)
3.0--5.0(325mesh)
Specific Area(g/m2) 350----450 450--600 450--600
Note

Refractory High alumina cement A600 A700 A900

High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30

High Aluminum Cement Notes:
1.In the construction process, in order to control condensation time, mixed with Portland cements, limestone or any other raw material can produce Calcium hydroxide is strictly forbidden. Tools and equipment must be washed clean before using.
2.Mixing water PH should be around 7.
3.Alkali project can't be applied in.
4.Water reducing agent must be tested before using
5.Pay attention to Aggregate and powder material's particle size and chemical content and impurities ,Fe, S, Alkali, Cl-­, should also be specially noted.
6.Do not mixed with other raw material when transported.

Application

Refractory High alumina cement A600 A700 A900

High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30

Calcium High Aluminum Cements is used in making bulk refractory material,refractory castables and fire brick.And widely used for making various furnaces refractories in metallurgical industry,chemical industry,petroleum industry,electrical industry,machinery industry,building materials industry.It is also used in project of emergency repairing and emergency construction as well as chemical building materials for special using.
We can offer high alumina cement with different fineness as per the customers' requirements.
High Aluminum Cements Testing method
Chemical Composition:According with GB/T205 for "High Alumina Cement".
Blaine:According with GB/T8074 for "High Alumina Cement".
Fineness:According with GB/T1345 with screen of 0.045mm for "High Alumina Cement"..
Setting time:According with the addenda A of GB/TGB201-2000 for "High Alumina Cement"

Package and delivery

Refractory High alumina cement A600 A700 A900

Packing:
Adopted specified by GB9774 cement packing sack,25kg or 50kg in PE bag with a complex bag of woven plastic and kraft paper outside.Other kind of bags can be supplied according with the agreements of the buyer and the seller.

Shipping information of calcium aluminate high alumina refractory cement:
1. FEDEX/DHL/UPS/TNT for samples.
2. By Sea for batch goods.
3. Delivery time: within 25 days
Note:
Keep in dry conditions and prevent humidity during storage and transportation.Don't mix other variety of cements.

FAQ

Our calcium aluminate high alumina refractory cement quality assurance:
1. Inspection and Control of incoming raw materials
2.Inspection and control of the process
3.Inspection of product Standardization of quality of each product by process control and experimentation.
4.Taking corrective measures whenever deviations are noted.
5.Quality audit by quality management.
6.ISO 9001 Certification.
Why choose us!
The advantages of our company:
1. High quality: Strict quality control and more than 10 years experiences.
2. Competitive price: Directly from our factory to your hands without other traders.
3. Good packaging: Avoid damage and secure your goods in transportation.
4. Quick response: Your any questions will be replied within 24 hours.
5. Professional technology: The size, density, chemical composition of calcium aluminate high alumina refractory cement can be customized.
6. Geographical advantage: Our factory is located in Zhengzhou Henan province, which is one of the main refractory production bases in China. we have abundant resources and high quality minerals. This favorable condition reduce the cost to save you money.
7. Timely delivery: 25 days after receiving deposit.
8. Samples are free.

Contact

High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30

Product tags

lithium tantalate wafers

,

cement silo capacity

,

42.5r portland cement
Send your message to this supplier
Send Now

High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30

Ask Latest Price
Watch Video
Product Detail
Place of Origin :
Henan, China
Shape :
Powder
Material :
Diatomite
SiO2 Content (%) :
≤8.0%
Al2O3 Content (%) :
≥50~70
CaO Content (%) :
30% ~ 39%, 30% ~ 39%
Contact Supplier
video
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30
High Alumina Cement A600 A700 A900 Compressive Strength MPa ≥80 Setting Time Min 30

Henan Hongtai Kiln Refractory Co.,Ltd.

Verified Supplier
1 Years
henan, zhengzhou
Since 2012
Business Type :
Manufacturer
Main Products :
High Alumina Brick, AZS Refractory Bricks, Fire Clay Brick
Total Annual :
10000000-50000000
Employee Number :
100~200
Certification Level :
Verified Supplier
Discover similar products
View More

Find Similar Products By Category:

Supplier Homepage Products Other Refractory Products
MachineU China Products Chemicals Inorganic Chemicals Non-Metallic Products Refractory
Contact Supplier
Submit Requirement