Description of Magnesia-Ferro-Spinel Bricks
Magnesia-iron spinel bricks are made of bivalent iron aluminum spinel (FeO Al2O3) and high-purity magnesia as the main raw materials. During the firing process, the firing temperature and firing atmosphere are strictly controlled to ensure that the iron in the brick is oxidized. The substance exists in the form of FeO.
During the use of mafic-iron spinel bricks, a layer of highly viscous calcium-iron and calcium-iron-aluminum compounds is formed on the hot surface of the brick, which is easy to hang on the kiln. In addition to the excellent kiln-hanging properties of magnesia-chrome bricks, magnesia-iron spinel bricks also have higher thermomechanical and thermochemical properties.
Sprcifications of Magnesia-Ferro-Spinel Bricks
| Iterm | Indicators | |
| MgO% | ≥ | 85 |
| Fe2O3% | 5-7.5 | |
| Al2O3% | 3-5 | |
| SiO2% | ≤ | 2 |
| Bulk Density (g/cm3) | ≥ | 3 |
| Apparent Porosity % | ≤ | 17 |
| Cold Crushing Strength (Mpa) | ≥ | 45 |
| Refractoriness under Load T0.6 (℃) | ≥ | 1600 |
| Thermal shock resistance(1100℃ water quenching,cycle) | ≥ | 6 |
| Thermal conductivity coefficienW/m.k | ≤ | 2.6 |
Packing of Magnesia-Ferro-Spinel Bricks
1.on wooden pallets with plastic cover: wooden pallet size :930*930 or 1000*1000mm,
2.Load weight of each pallet: 1.5-2.0 tons,
3.230*114*65mm:512PCS/Pallet, 230*114*75mm:448PCS/Pallet.
Shipping of Magnesia-Ferro-Spinel Bricks
1.Our packaging is as per customer’s request
2.Normal goods delivered by sea transport
3.Sample shipping by express
4.We will shipping and delivery goods timely, quanlity and quantity guaranteed, and also in accordance with the contract and customer's requirment completely.