3511(HTU-3315) UV curing adhesiveIt is a single component, high viscosity, medium intensity ultraviolet curable adhesive. For plastic and plastic bonding.

Typical Applications

Plastics and plastic bonding, suitable for bonding between PC material, especially recommended for the adhesive sealing plug guardrail.

Before solidification characteristics

Typical values

Appearance Amber transparent liquid

Viscosity (mPa.s) (GB / T2794-1995) 3300 ~ 4300

Density (g.cm -3) (GB / T13477-2002) 1.05

Binders Chemical Type Modified acrylate

solidifying feature

Typical values

Light intensity (W) (high pressure mercury lamp) 1000 to 2000

Curing energy (mj / cm2) 400

After curing characteristics

Uv curing performance indicators (1000W Light curing40s)

Typical values

The glass transition temperature (Tg) (℃) 70

Hardness (Shore D) (ASTM D 2240) 62

Thermal expansion coefficient

@ 25 ℃ (℃ -1) 160 × 10-6

@ 80 ~ 120 ℃ (℃ -1) 200 × 10-6

Working temperature (℃) -30 ~ 90

Mechanical properties after UV curing

Typical values

Tensile strength (PVC / PVC) (MPa) 10

(ASTM D2095)

(Curing conditions: 40s @ 100mW / cm2,365nm)

Adhesive torsional strength (PC / PC) (Nm) 110

(Curing conditions: 40s @ 100mW / cm2,365nm)

(ASTM D3658)

Instructions

Sticky surfaces should be dry and free of grease.

When applied to the adhesive curing light intensity is not less than 40mW / cm2, applied to the surface coating time strength of not less than 100mW / cm2.

Notes

Do not have poured glue and then rewind original packaging to avoid contamination glue.

Store away from children.

This pair of eyes, a slight skin irritation. If it does not accidentally splashed into the eyes, flush immediately with plenty of water. If contact with skin, wash immediately with soap. In serious cases see a doctor.

Product safety information, please refer to the product MSDS.

Packing Specifications

Order number: 351106,1Kg/bucket,12bucket/box.

storage condition

From light in a dry environment at room temperature 10 ~ 26 ℃.

Storage period of 12 months.