Product Description:

The Layered Zirconia product is a top-of-the-line dental material that offers exceptional performance and durability for various dental applications. This product is meticulously designed to meet the highest standards of quality and functionality, making it an excellent choice for dental professionals and patients alike.

One of the key features of the Layered Zirconia product is its sintering temperature range of 1350-1450°C. This temperature range ensures that the material is well-bedded and achieves optimal strength and stability during the manufacturing process. As a result, the final product exhibits superior mechanical properties and longevity, making it a reliable option for long-term use.

Furthermore, the Layered Zirconia product boasts a layer thickness of 0.3-0.5mm, providing a perfect balance between strength and aesthetics. The thin layers allow for precise customization and natural-looking restorations, enhancing the overall appearance of the final prosthetic.

The manufacturing process of the Layered Zirconia product involves CAD/CAM milling, a cutting-edge technology that ensures exceptional accuracy and consistency in the production of dental restorations. This advanced manufacturing process guarantees a high level of precision and detail, resulting in perfectly fitted restorations that meet the unique needs of each patient.

When it comes to chemical composition, the Layered Zirconia product is composed of ZrO2 + Y2O3, a combination that offers excellent biocompatibility and durability. This composition ensures that the material is resistant to wear and corrosion, maintaining its integrity and aesthetics over time.

In addition, the Layered Zirconia product exhibits a coefficient of thermal expansion of 10.5-11.5 X 10^-6 K^-1, which is essential for ensuring compatibility with the natural tooth structure. This optimal thermal expansion coefficient minimizes the risk of fractures and chipping, providing long-lasting durability and reliability for dental restorations.

Overall, the Layered Zirconia product is a premium dental material that excels in both functionality and aesthetics. With its well-bedded sintering process, wear resistance of the porcelain layer, and high aesthetics, this product offers a superior solution for a wide range of dental applications. Dental professionals can trust in the quality and performance of the Layered Zirconia product to deliver exceptional results and patient satisfaction.

Technical Parameters:

Applications:

Product Application Occasions and Scenarios for Joydeta Dental Biomimetic Layered Zirconia:

The Joydeta Dental Biomimetic Layered Zirconia, originating from China, is a cutting-edge dental material known for its exceptional quality and performance.

With a density ranging from 6.0 to 6.1 G/cm3, this zirconia offers superior strength and durability, making it ideal for a wide range of dental applications.

The transparent color of this zirconia adds to its aesthetic appeal, making it perfect for use in creating natural-looking dental restorations.

Thanks to its well-bedded layer thickness of 0.3-0.5mm, Joydeta Dental Biomimetic Layered Zirconia allows for precise and detailed dental work, ensuring optimal results for patients.

Its coefficient of thermal expansion, between 10.5 and 11.5 x 10^-6 K^-1, ensures stability and compatibility with natural teeth, reducing the risk of fractures or damage.

When it comes to sintering, this zirconia requires a temperature of 1350-1450°C, ensuring proper fusion of layers and optimal mechanical properties.

Overall, the Joydeta Dental Biomimetic Layered Zirconia is a versatile and reliable material suitable for various dental applications, including crowns, bridges, and implants.

Whether in a dental clinic or laboratory setting, this zirconia excels in providing high-quality, well-bedded restorations that meet the needs and expectations of both dental professionals and patients.

Customization:

Product Customization Services for the Layered Zirconia:

Brand Name: Joydeta

Model Number: Dental Biomimetic Layered Zirconia

Place of Origin: China

Color: White

Material: Zirconia

Chemical Composition: ZrO2 + Y2O3

Density: 6.0-6.1 G/cm3

Flexural Strength: 900-1200 MPa

Description: High aesthetics, well-bedded, Wear resistance of porcelain layer