50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts
50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts
50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts
50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts
50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts
50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts
50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts
50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts
Specifications
Brand Name :
PRM
Model Number :
custom
Certification :
ISO9001
Place of Origin :
China
MOQ :
1kg
Price :
$50~200/kg
Payment Terms :
T/T
Supply Ability :
2000kgs/month
Delivery Time :
15~20 work days
Packaging Details :
plywood case
Name :
50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts
Grade :
WMo alloy
Mo content :
50%（wt%）
Thickness :
0.3~25mm
Width :
50~600mm
Length :
≤2500 mm
Surface :
polished, alkaline, washing sandblasting
Export port :
any port in China
Standard :
ASTM B386
Description

50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts

1. Description of 50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts:

Molybdenum-tungsten alloy plate is the most commonly produced product among molybdenum-tungsten products. Because molybdenum-tungsten alloy has good high temperature performance, good thermal conductivity, electrical conductivity, low thermal expansion coefficient and high temperature strength, most of them are used in electronic power equipment manufacturing, Metal material processing industry, glass manufacturing, high temperature furnace structural component manufacturing, aerospace and defense industry.

The melting point of molybdenum-tungsten alloy plate increases with the increase of tungsten content. When the tungsten content increases to 25%, the melting point of the alloy is about 200℃ higher than that of pure molybdenum (as shown in the figure below). Therefore, the corresponding alloy composition can be selected in the range of 2620-3410 °C according to the use temperature and the required melting point of the alloy. This advantage is also one of the advantages that molybdenum-tungsten alloys are widely used. The relationship between the content of tungsten in molybdenum-tungsten alloy and the melting point of the alloy is shown in the figure below.

50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts

50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts

2. Size of 50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts:

Thickness :0.3~25mm

Width:50~600mm

Length: ≤2500 mm

Also we can produce as per customer's drawing ,processing various special-shaped parts.

Standard of produce: ASTM B386

3. Hardness of 50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts:


The highest room temperature hardness value of molybdenum-tungsten alloy is between 90% and 100% of tungsten content, and its Vickers hardness value is as high as 3530-3860MPa, which is more than double that of pure molybdenum. The highest high temperature hardness value of the alloy is between 70% and 85% tungsten content. When the tungsten content increases from O to 40%, the room temperature tensile strength of the as-processed molybdenum-tungsten alloy increases from 617MPa to 900MPa.

4. Common defects and elimination methods of 50%Mo Molybdenum Tungsten Alloy Plate:

Defects Causes Elimination method
Surface crack 1) Surface oxide scale and getter layer are not removed
2) The slab thickness is uneven, causing serious uneven deformation
3) The surface cooling is too fast and the plasticity is reduced
4) The heating temperature is uneven and the surface temperature is too low
5) The distribution of the deformation amount of the pass is uneven, and it is suddenly large and small		 1) Strictly control the surface quality
2) The shape of the slab is regular and the size is uniform
3) Used Preheat rolls to prevent the surface of the rolling stock from cooling down too quickly
4) Heating evenly
5) Reasonably distribute the deformation amount of the pass.
Pit 1) The heating temperature is too high or the time is too long
2) The scale is peeled off and pressed into the surface		 1) Strictly control the heating temperature and time
2) Control the final rolling temperature to prevent the oxide scale from falling off.
Surface crater 1) The burrs on the edge of the board are pressed into the surface of the board
2) The heat-resistant material in the furnace is pressed into the surface when rolling
3) There are foreign objects on the board that are pressed into		 1) Clear the board flash and burr in time
2) Remove foreign matter on the surface of the board in time
3) Timely replacement of rolls
Scratch Adhesion or burrs on guide plate, roller table, guide rule, roller When rolling, pay attention to check the surface and remove the bond in time
Cracked edge 1) The slab temperature is uneven and the edge temperature is low
2) Improper configuration of the roll shape and tilting when feeding
3) The deformation of the pass is too large		 1) The heating temperature should be uniform and the operation speed should be fast
2) Adjust the roll shape, and feed it in the correct direction.
3) Control the amount of pass deformation

Do you want to know more about our products?

50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts

50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts

Send your message to this supplier
Send Now

50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts

Ask Latest Price
Product Detail
Brand Name :
PRM
Model Number :
custom
Certification :
ISO9001
Place of Origin :
China
MOQ :
1kg
Price :
$50~200/kg
Contact Supplier
50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts
50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts
50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts
50%Mo Molybdenum Tungsten Alloy Plate For High Temperature Parts

Shaanxi Peakrise Metal Co.,Ltd

Site Member
2 Years
Shaanxi, baoji
Business Type :
Manufacturer, Exporter
Main Products :
Molybdenum Tungsten Alloy, Tungsten Copper Alloy, Molybdenum Copper Alloy
Certification Level :
Site Member
Discover similar products
View More