Online Shop Hot Sale Flat Lamination Bonding Reactive PUR Hot Melt Glue WANLI® PUR-886 Yellow Solid with Viscosity About 5000mPa·s@160℃(Brookfield-ASTMD3236) And Excellent Initial & Final Bonding Strength After Curing

Wanli® PUR hot melt adhesive PUR-886 for flat lamination bonding is a single-component reactive PUR hot melt adhesive with 100% solid content. PUR-886 can be used for the bonding of various wood base, EVA foam, PC foam and other substrates. PUR-886 has higher initial strength for PVC, leather, veneer, PET , melamine impregnated paper and other surface materials. PUR-886 is featured stable viscosity under heating at a certain temperature, high initial bonding strength and final strength. After curing, PUR-886 has good peel strength, good heat and humidity resistance and chemical resistance..

APPLICATION

Wanli® PUR hot melt adhesive PUR-886 is used for flat lamination bonding. PUR-886 can be used for the bonding of various wood base, EVA foam, PC foam and other substrates. PUR-886 has higher initial strength for PVC, leather, veneer, PET , melamine impregnated paper and other surface materials.

FEATURE

Stable viscosity under heating at a certain temperature.

High initial bonding strength and final strength.

PUR-886 has good peel strength, good heat and humidity resistance and chemical resistance after curing.

USER GUIDE

The package of PUR-886 is suitable for various dispensing equipment.

The recommended operating temperature is 160±5℃.

In order to achieve complete curing, it is better to place finished product in a working environment with suitable temperature and humidity (recommended temperature: 23~25℃, about 65% relative humidity).

STORAGE

Store the product where it’s dry, cool and avoid direct sunlight. The storage temperature should be no more than 35℃ and avoid open fire or heat source.