Hot Selling Online Shop White To Yellowish Solid PUR Hot Melt Adhesives WANLI® PUR-1932F with Viscosity About 4000mPa·s@140℃(Brookfield-ASTMD3236) For Flat Lamination Bonding of Various Wood-based, Plastic, Metal And Other Substrates

Wanli® PUR hot melt adhesive PUR-1932F for flat lamination bonding is a single-component reactive PUR hot melt adhesive with 100% solid content. Reactive polyurethane hot melt adhesive PUR-1932F has high initial strength for PVC, PETG, PMMA, pet, melamine impregnated paper and other surface materials. PUR-1932F can be used for the bonding of various wood-based, plastic, metal and other substrates. PUR-1932F is featured stable viscosity under heating at a certain temperature, high initial bonding strength and final strength. After curing, PUR-1932F has good peel strength, good heat and humidity resistance and chemical resistance, resistant to boiling for 3 hours.

APPLICATION
Wanli® PUR hot melt adhesive PUR-1932F is used for flat lamination bonding. Reactive polyurethane hot melt adhesive PUR-1932F has high initial strength for PVC, PETG, PMMA, pet, melamine impregnated paper and other surface materials. It can be used for the bonding of various wood-based, plastic, metal and other substrates.

FEATURE
Stable viscosity under heating at a certain temperature.
High initial bonding strength and final strength.
PUR-1932F has good peel strength, good heat and humidity resistance and chemical resistance after curing.

USER GUIDE
The package of PUR-1932F is suitable for various dispensing equipment.
The recommended operating temperature is 110℃~140℃.
In order to achieve complete curing, it is better to place finished product in a working environment with suitable temperature and humidity (recommended temperature: 23~25℃, about 65% relative humidity).

STORAGE
Store the product where it’s dry, cool and avoid direct sunlight. The storage temperature should be no more than 35℃ and avoid open fire or heat source.