UNS N08020 ALLOY 20 Strips Coil High Performance ,High Tem, High Corrosion Resistant Slit Coil overview

Alloy 20 is an austenitic stainless steel possessing excellent resistance to attack by sulfuric acid and many other aggressive environments. Alloy 20 stainless is also stabilizes to limit inter-granular attack, even in the sensitized condition. Important advantages of alloy 20 stainless are its excellent mechanical properties and comparative ease of fabrication. The presence of Columbium in the alloy minimizes the precipitation of carbides during welding.

PRODUCT FORMS:

Sheet, plate , Strip, pipe ,tube ,bar ,profiles

UNS N08020 Alloy 20 stainless steel Equivalent Materials

ASTM N08020
ASTM F20
UNS N08020

UNS N08020 ALLOY 20 Strips Coil Slit Coil Specification and Dimension Ranges

WHAT INDUSTRY SPECIFICATIONS IS AL-6XN STAINLESS STEEL STRIP MANUFACTURED TO

Shaped, Flat, Square, Round, Fine Wire, Plated and Bare Wire ASTM A240, ASTM A265, ASTM B 463, ASTM B471, ASTM B 472, ASTM B 473, ASTM B475

Alloy 20 STRIP coil Dimension Ranges:

Standard: ASTM/EN/JIS
Thickness: 0.1mm-4.0 mm For cold rolled

Thickness: 0.1mm-10 mm For Hot rolled rolled

Width: 1.5mm-1200 mm
Length: coil type or it can be produced as customer requirements
Surface Finish: NO.1, 2B, 2H(Rerolled Bright), BA, No.4, 8K (Mirror), HL (Hairline), Polishing Bright, etc
Edge: Mill Edge, Slit Edge, Deburred Edge, Round Edge, V Type Edge

Condition :

ANNEALED CONDITION

Ultimate Tensile Strength: 95 KSI min (655 MPA min) Yield Strength (0.2% Offset): 38 KSI min (260 MPA min) Elongation: 40%min Hardness: B95 max

TEMPERED 1/16 HARD

Ultimate Tensile Strength: 95 KSI min (655 MPA min) Yield Strength (0.2% Offset): 45 KSI min (310 MPA min) Elongation: 40% min

Tempered 1/8 Hard Ultimate Tensile Strength: 100 KSI min (690 MPA min) Yield Strength (0.2% Offset): 55 KSI min (380 MPA min) Elongation: 45% min

TEMPERED 1/4 HARD

Ultimate Tensile Strength: 125 KSI min (860 MPA min) Yield Strength (0.2% Offset): 75 KSI min (515 MPA min) Elongation: 25% min

TEMPERED 1/2 HARD

Ultimate Tensile Strength: 150 KSI min (1035 MPA min) Yield Strength (0.2% Offset): 110 KSI min (760 MPA min) Elongation: 15% < 0.15" 18% > 0.15"

TEMPERED 3/4 HARD

Ultimate Tensile Strength: 175 KSI min (1205 MPA min) Yield Strength (0.2% Offset): 135 KSI min (930 MPA min) Elongation: 10% < 0.15" 12% > 0.15"

TEMPERED FULL HARD

Ultimate Tensile Strength: 185 KSI min (1275 MPA min) Yield Strength (0.2% Offset): 140 KSI min (965 MPA min) Elongation: 8% < 0.15" 9% > 0.15"

Available Steel Grade:

Stainless steel : Type 201, 202, 205, 301, 302, 302B, 303, 303Se, 304, 304L, 302HQ, 304N, 305, 308, 309, 309S, 310, 310S, 314, 316, 316L, 316F, 316N, 317, 317L, 317LMN, 321, 330, 347, 348, 384, 405, 409, 429, 430, 430F, 430FSe, 434, 436, 442, 446, 403, 410, 414, 416, 416Se, 420, 420F, 422, 431, 440A, 440B, 440C, 630 , 13-8 PH ,15-5 PH , 17-7 PH ,17-4 ph , 904L , A286 ,VG-10 , SAE 316 , SAE 316L , SAE 440 , SAE 420

Duplex stainless steel : 2205 , 2304 , 2507

Nickel alloy :

Titanium and titanium alloys

UNS N08020 ALLOY 20 Strips Coil High Performance ,High Tem, High Corrosion Resistant Slit Coil Application

UNS N08020 ALLOY 20 Strips Coil Slit Coil Technical datasheet

CHEMISTRY TYPICAL

Carbon: 0.070 max
Manganese: 2.00 max
Copper: 3.00-4.00
Chromium: 19.00-21.00
Nickel: 32.50-38.00
Molybdenum: 2.00-3.00
Sulfur: 1.00 max
Columbium +Tantalum: 8 x C min-1.00 max
Phosphorus: 0.035 max
Iron: Balance

PHYSICAL PROPERTIES

Density, 0.292 lbs/in³, 9.01 g/cm³

Electrical Resistivity: microhm-in, (microhm-cm): 68°F (20°C): 28.4 (72)

Specific Heat: BTU/lb/°F (kJ/kg•K):
32-212°F (0-100°C): 0.12 (0.50)

Thermal Conductivity: BTU/hr/ft²/ft/°F (W/m•K):
At 212°F: 7.57 at 752°F: 10.5

Mean Coefficient of Thermal Expansion: in/in/°F
77-212°F: 8.16 x 10
77-600°F: 8.84 x 10
77-1652°F: 9.53x 10

Modulus of Elasticity: KSI (MPa) 29.0 x 10³ (200 x 10³) in tension 11.0 x 10³ (0.78 x 10³) in torsion

Magnetic Permeability:=200: Annealed < 1.02

MECHANICAL PROPERTIES AT ROOM TEMPERATURE
PROPERTIES: ANNEALED

Ultimate Tensile Strength: 80 KSI min (551 MPa min)
Yield Strength (0.2% offset): 35 KSI min (241 MPa min)
Elongation: 30% min (gauges: >0 .015 inches)
Hardness: Rb 95 max < strong>Properties: Tempered

Alloy 20 CB-3 can be cold rolled to achieve the temper properties required by specific
customers and/or manufacturing requirements.

AL-6XN UNS N08367 Stainless Steel Strip Astm A182 Products display and Package Details

UNS N08020 ALLOY 20 Strips Coil Slit Coil Equivalent