ALLOY 188 Haynes 188 Equivalent ,Cobalt Alloy , Ams 5608 UNS R30188 Overview

ALLOY 188 Haynes 188 Equivalent ,Cobalt Alloy , Ams 5608 UNS R30188 Application :

ALLOY 188 Haynes 188 Equivalent ,Cobalt Alloy , Ams 5608 UNS R30188 Technical datasheet

Typical Room Temperature Mechanical Properties of annealed alloy 188 Sheet < Hayes 188 equivalent >

Principal Features
Excellent High-Temperature Strength and Environment Resistance
188 alloy (UNS R30188) is a cobalt-nickel-chromium-tungsten alloy that com-bines excellent high-temperature strength with very good resistance to oxidizing environ-ments up to 2000°F (1095°C) for prolonged exposures, and excellent resistance to sulfate deposit hot corrosion. It is readily fabricated and formed by conventional techniques, and has been used for cast component. Other attractive features include excellent resistance to molten chloride salts, and good resistance to gaseous sulfidation.
Readily Fabricated
188 alloy has good forming and welding characteristics. It may be forged or oth-er hot-worked, providing that it is held at 2150°F (1175°C) for a time sufficient to bring the entire piece to temperature. As a consequence of its good ductility, 188 alloy is also readily formed by cold working. The alloy does work-harden rapidly, however, so frequent inter-mediate annealing treatments may be needed for complex component forming operations. All hot- or cold- worked parts should be annealed and rapidly cooled in order to restore the best balance of properties.
The alloy can be welded by both manual and automatic welding methods, including gas tungsten arc (TIG), gas metal arc (MIG), electron beam and resistance welding. It exhibits good restraint welding characteristics.
Heat Treatment
Wrought 188 alloy is furnished in the solution heat treated condition, unless oth-erwise specified. The alloy is normally solution heat-treated at 2125-2175°F (1163-1191°C) and rapidly cooled or water quenched for optimal properties.
Annealing at temperatures less than the solution heat-treating temperature will produce some carbide precipitation in alloy 188, which may affect the alloy’s properties,

General Q and A

Q: Would you provide samples For free?

A: Yes. with on stock specification We provide samples For Free. Freight charge collect

Q: What information should i provide to source for the right products?

A: Material grade, width, thickness, coating and Purchase quantity, Expected lead time, etc

Q: What are the shipping ports?

A: Under normal circumstances, we ship from Shanghai, Tianjin, Qingdao, Ningbo ports, you

can choose other ports according to your needs.

Q: About product prices?

A: Prices vary from period to period due to cyclical changes in the price of raw materials.

Q: How long does your delivery time take?

A: In general, our delivery time is within 5-45 days, and may be delayed if the demand is extremely

large or special circumstances occur.

Q: Can I visit your location?

A: Of course, we welcome customers from all over the world to visit our factory. However, some

of the plants are not open to the public.

Q: Does the product have quality inspection before loading?

A: Of course, all our products are strictly tested for quality before packaging, and unqualified products will be destroyed. We provide All Original Mill test certificate and support third party inspection.

Q: How to pack the products?

A: The inner layer has a waterproof paper outer layer with iron packaging and is fixed with a fumigation

wooden pallet. It can effectively protect products from corrosion during ocean transportation.

Q: What is your working time?

A: In general, our online service time is Beijing time: 8:00-22:00, after 22:00,

we will reply to your inquiry during the next working day.