CuCo1Ni1Be CW103C Cobalt Nickel Copper Beryllium round rod

Product Description
CuCo1NiBe Details:CuCo1Ni1Be CW103C Cobalt Nickel Beryllium Copper CuCo1Ni1Be—CW103C (DIN 2.1285) Cobalt Nickel Beryllium Copper Alloy contains approximately 1% Cobalt, 1% Nickel and 0.5% Beryllium. After hot forging and heat treatment processes this material gains considerably hardness, electrical and thermal conductivity as well. It is possible to have different combinations of electrical conductivity and hardness by changing the heat treatment conditions；CuCo1Ni1Be also Offers good strength and hardness characteristics coupled with conductivity in the range of 45-60 percent of copper with ultimate tensile and hardness properties approaching 140 ksi and RB 100 respectively, all of its properties are quite the same as CuCo2Be-C17500 and CuNi2Be-C17510.

Product Feature
Chemical Composition: Be: 0.40-0.70%Co: 0.80-1.30%Ni: 0.80-1.30%Cu: BalanceNote: Copper plus additions equal 99.5% minimum. Typical Physical Properties:Density (g/cm3): 8.83Density before age hardening (g/cm3): 8.75Elastic Modulus (kg/mm2 (103)): 14.10Thermal Expansion Coefficient (20 °C to 200 °C m/m/°C): 17 x 10-6Thermal Conductivity: 209 W/m • oK at 20 CMelting Range (°C): 1000-1070 Note: 1). the units are based upon Metric.2). the typical physical properties apply to age hardened products.

Product Specification/Models
International Specification: Rods/Bars/Tubes: ASTM B441, SAE J461,463; RWMA Class 3Sheets: ASTM B534Wires: ASTM B441Plates: ASTM B534, SAE J461,463; RWMA Class 3 European Standards: CuCo1Ni1Be, DIN 2.1285; CW103C to EN Note: ASTM: American Society for Testing and Materials SAE: Society of Automotive Engineers AMS: Aerospace Materials Specification (Published by SAE) RWMA: Resistance Welder Manufacturers' Association Note: Unless otherwise specified, material will be produced to ASTM.