Dip Spin Zinc Flake Coating With Microlayer Corrosion Protection

1 Zinc Flake Coating Information

Trade Name: Zincover

Article/Model No.:JH-9382

2 Composition/information on ingredients

JH-9382 is made up of three packs: A,B and C;

Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and organic additive.

Pack B: It is water solution that mainly combined with corrosion protecion additive, particular regulator water solution etc.

Pack C: It is the tackifier of the coating which mainly made up of cellulose white or yellowish powder.

3 Coating Process

3.1 Mix Ratio

Pack A:16.0 kg

Pack B:24.0 kg (the quantity can be increased appropriately if spray coating)

Pack C:0-50 g (according to different viscosity demand )

3.2

3.3

3.4

Stir the mixture about 1~2 hours fast after B added, then add C. C should be powdered if lump exist.(The barrel temperature should not be lower than 30℃, otherwise C will not be dissolved sufficiently .)Then stir 12 hours continuously.

3.5

The coating should be filtrated by 100 mesh stainless steel screen before pouring into dip barrel.

v

3.6

Temperature control device should be equipped with dip barrel to keep the temperature of coating at 22±2℃.(If temp. is too high, the paint is liable to deteriorate, and viscosity will be effected.) The coating should be stirred circularly to keep evenly dispersed.

3.7

Test Specific gravity,PH,Temperature,Viscosity of coating every 8 hours if operate continuously.

5 Technical data

6 Mix Diagram

Caution: Temperature should be controlled in above operation.

7 Packing

(For special packaging)

10 Quality guarantee period

Before compound 6 months at 20℃

After compound 30 days at 20℃ ( It can be recycled if adding fresh coating continuously. )

It should be stored under 20℃ if not in use.